Thermal and Microstructure Analysis of Cocofoam Made from Blended Coconut Fiber with Latex Compound

  • I.D.K. Anom
Keywords: Cocofoam, latex compound, coconut fiber, scanning elestron micro (SEM), thermal analysis

Abstract

Thermal and microstructure analysis of cocofoam made from vulcanized coconut fiber and latex compound were conducted. The cocofoam was produced by blending coconut fiber and latex compound with weight ratio of 10/25 (CF5-1) and 20/55 (CF5-2) at room temperature. The cocofoam characters were then analyzed by Scanning Electron Microscope (SEM), Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DTA) instruments. The result showed that the increase of coconut fiber and latex compound ratio produced a higher density of cocofoam. The highest value density was 0.6920 g/cm3 with flexibility of 90% produced by the CF5-2 sample. The SEM analysis showed that both specimens surface of the CF5-1 and CF5-2 samples have different pores size and the latex compound is not distributed thoroughly in the cocofoam. The thermal analysis showed that the production of cocofoam was largely determined by latex compound that served as fiber binder matrix. Cocofoam started to degrade at the temperature of 90oC and was damaged when it was heated at the temperature of 115oC for 2.5 hours.

Author Biography

I.D.K. Anom

Department of Chemistry, Faculty of Mathematics and Natural Sciences, Manado State University, Indonesia

References

[1] Boimau, K. 2010. Pengaruh Fraksi Volume dan Panjang Serat Terhadap Sifat Bending Komposit Poliester yang Diperkuat Serat Batang Pisang, Seminar Nasional Tahunan Teknik Mesin (SNTTM) ke-9, Palembang 13-15 Oktober 2010.
[2] Diharjo, K. 2006. Pengaruh Perlakuan Alkali terhadap Sifat Tarik Bahan Komposit Serat Rami-Polyester, Jurnal Teknik Mesin, 8 (1), 8-13.
[3] Hadiyawarman, A. Rijal, B.W. Nuryadin, M. Abdullah and Khairurrijal. 2008. Fabrikasi Material Nanokomposit Superkuat, Ringan and Transparan Menggunakan Metode Simple Mixing, Jurnal Nanosains & Nanoteknologi, 1 (1), 14-21.
[4] Sudarsono, T. Rusianto and Y. Suryadi. 2010. Pembuatan Papan Partikel Berbahan Baku Sabut Kelapa dengan Bahan Pengikat Alami (Lem Kopal), Jurnal Teknologi, 3 (1), 22-32.
[5] Mahmud, Z. and Y. Ferry. 2005. Prospek Pengolahan Hasil Samping Buah Kelapa. Jurnal Perspektif, 4 (2), 55-63.
[6] Arbintarso, E.S. 2009. Tinjauan Kekuatan Lengkung Papan Serat Sabut Kelapa Sebagai Bahan Teknik, Jurnal Teknologi, 2 (1), 53-60.
[7] Maulida. 2008. Pembuatan Komposit Termoplastik Berdasarkan Serat Kelapa Sawit dengan Kaedah Pragpreg, Jurnal Penelitian Rekayasa, 1 (2), 74-79.
[8] Anggaravidya, M. 2008. Pengaruh Jenis Blowing Agent Terhadap Sifat Fisik Busa Karet, M.P.I., 2 (3), 277-283.
[9] Mills, N.J. 2007. Polymer Foam Handbook: Engineering and Biomechanics Applications and Design Guide, Butterworth - Heinemann: Elsevier, burlington.
[10] Najib, N.N., Z.M. Ariff, N.A. Manan, A.A. Bukar and C.S. Sipaut. 2009. Effect of Blowing Agent Concentration on Cell Morphology and Impact Properties of Natural Rubber Foam, J. Phys. Sci., 20 (1), 13-25.
[11] Rusianto, T., and L.D. Setyana. 2005. Pengaruh Kadar TiO2 Terhadap Kekuatan Bending Komposit Serbuk Al/TiO2, Jurnal Teknik Mesin, 7 (1), 28-34.
[12] Li, X., G. Lope, Tabi and S. Panigrahi. 2007. Chemical Treatments of Natural Fiber for Use in Natural Fiber-Reinforced Composites: A Review, J. Polym. Environ, 15, 25-33.
[13] Lee, E.K., and S.Y. Choi. 2007. Preparation and Characterization of Natural Rubber Foams: Effects of Foaming Temperature and Carbon Black Content, J. Chem. Eng., 24 (6), 1070-1075.
[14] Feldman, D., and A.J. Hartomo. 1995. Bahan Polimer Konstruksi Bangunan, PT Gramedia Pustaka Utama, Jakarta.
[15] Stevens, M.P., and L. Sopyan. 2007. Kimia Polimer, Pradnya Paramita, Jakarta.
[16] Sudirman, Ridwan, Mujamilah, and W. Trijono. 2000, Analisis Termal and Struktur Mikro Magnet Komposit Berbasis Heksaferit dengan Matriks Karet Alam, Jurnal Sains Material Indonesia, 2 (1), 13-17.
Published
2013-04-01
How to Cite
I.D.K. Anom. (2013). Thermal and Microstructure Analysis of Cocofoam Made from Blended Coconut Fiber with Latex Compound . CORD, 29(1), 9. https://doi.org/10.37833/cord.v29i1.93
Section
Articles